Sanmac 316L (Hollow Bar) (UNS S31603)


Sanmac®  316L is a molybdenum-alloyed austenitic stainless steel bar with improved machinability. The addition of Mo provides the product with much improved corrosion resistance compared with Alloy 304, particularly with respect to pitting and crevice corrosion in chloride environments. Sanmac 316L resists atmospheric corrosion as well as moderately oxidizing and reducing environments. It also resists corrosion in polluted marine atmospheres. The alloy has excellent resistance to intergranular corrosion in the as-welded condition.


It also provides higher creep, stress-to-rupture and tensile strength at elevated temperatures than a basic Alloy 304. As a fully austenitic grade it possesses excellent toughness, even down to cryogenic temperatures. This low carbon version of Alloy 316 is immune from the sensitisation caused by the precipitation of carbides at grain boundaries when heated, resulting in its widespread use in larger section welded components. It is readily formed and machined, although its relative toughness means that better machining is generally achieved at lower speeds with heavier feeds.


Sanmac® 316L has been developed to provide superior machinability as standard. Control of composition and inclusion type results in improved chip formation and reduced tool wear, providing great machining productivity and lower tool costs.

有关此产品的咨询,请致电我们 +44 (0)1782 610250



  • Higher resistance to pitting corrosion and crevice corrosion in seawater than Alloy 304 stainless steel
  • Pitting Resistance Equivalent number (PREN) of 25 compared with 19 for Alloy 304
  • Excellent ductility and impact strength at both ambient and sub-zero temperatures
  • Low carbon version of Alloy 316 thereby immune from grain boundary sensitisation
  • Excellent forming and welding characteristics
  • Non-magnetic except after significant welding or cold working


  • Process industry equipment in chemical containers, transport units, heat exchangers and organic & fatty acid production
  • Marine and shipbuilding piping, pumps, valves, fittings and marine architecture
  • Oil & Gas industry piping, valves, pumps, heat exchangers
  • Mining industry for woven screens
  • Machined parts for tube and pipe fittings


Cr Ni Mo Co Nb (+Ta) Ti V W Cu C Mn N Si P S Fe Al
最低限度 16.50 11.00 2.10
最大值 18.50 13.00 2.50 0.03 2.00 0.11 0.75 0.04 0.03 Bal


0.2% 证明力量 220 N/mm2 32.0ksi
抗拉强度, min 515 N/mm2 75.0ksi
Tensile strength, max 690 N/mm2 100.0ksi
伸长, 5.65√S0 and 4D 45%
Reduction of Area
硬度 <90
冲击强度 (室内温度) Typically >88J


  1. Testing shall be carried out in accordance with ASTM A370 or EN ISO 6892-1 (tensile), EN ISO 6506-1 (hardness)
  2. Minimum properties quoted (tested at room temperature in a longitudinal direction)
  3. Testing performed on each melt of material per heat treatment batch
  4. For hollow bar with wall thickness greater than 10mm (0.4”) the proof strength may fall short of the stated values by about 10MPa (1.4ksi)


密度 (Kg/m3) 8000
磁导率 (20°C) <1.05
Young’s Modulus (kN/mm2) 200
比电阻, 20°C (µΩ-m) 0.74
热膨胀, 20-100°C (m/m/°C) 16.5 x 10-6
比热, 20°C (J/kg.K) 485
导热系数, 20°C (W/m.K) 14