Specifications

  • UNS S31603
  • DIN 1.4404
  • X2 CrNiMo 17-12-2
  • JIS SUS316TKA
  • ASTM MT316L
View Data Tables For This Product

Sanmac 316L (Hollow Bar) (UNS S31603)

Sanmac®  316L is a molybdenum-alloyed austenitic stainless steel bar with improved machinability. The addition of Mo provides the product with much improved corrosion resistance compared with Alloy 304, particularly with respect to pitting and crevice corrosion in chloride environments. Sanmac 316L resists atmospheric corrosion as well as moderately oxidizing and reducing environments. It also resists corrosion in polluted marine atmospheres. The alloy has excellent resistance to intergranular corrosion in the as-welded condition.

 

It also provides higher creep, stress-to-rupture and tensile strength at elevated temperatures than a basic Alloy 304. As a fully austenitic grade it possesses excellent toughness, even down to cryogenic temperatures. This low carbon version of Alloy 316 is immune from the sensitisation caused by the precipitation of carbides at grain boundaries when heated, resulting in its widespread use in larger section welded components. It is readily formed and machined, although its relative toughness means that better machining is generally achieved at lower speeds with heavier feeds.

 

Sanmac® 316L has been developed to provide superior machinability as standard. Control of composition and inclusion type results in improved chip formation and reduced tool wear, providing great machining productivity and lower tool costs.

Langley alloys 316L

Specifications

  • UNS S31603
  • DIN 1.4404
  • X2 CrNiMo 17-12-2
  • JIS SUS316TKA
  • ASTM MT316L
View Data Tables For This Product

Data Tables

Chemical Composition:

CrNiMoCoNb (+Ta)TiVWCuCMnNSiPSFeAl
Min16.5011.002.10
Max18.5013.002.500.032.000.110.750.040.03Bal

Mechanical Properties:

0.2% Proof Stress220 N/mm232.0ksi
Tensile Strength, min515 N/mm275.0ksi
Tensile strength, max690 N/mm2100.0ksi
Elongation, 5.65√S0 and 4D45%
Reduction of Area
Hardness (Brinell)<90
Impact Strength (Room Temp)Typically >88J

Notes:

  1. Testing shall be carried out in accordance with ASTM A370 or EN ISO 6892-1 (tensile), EN ISO 6506-1 (hardness)
  2. Minimum properties quoted (tested at room temperature in a longitudinal direction)
  3. Testing performed on each melt of material per heat treatment batch
  4. For hollow bar with wall thickness greater than 10mm (0.4”) the proof strength may fall short of the stated values by about 10MPa (1.4ksi)

Physical Properties:

Density (Kg/m3)8000
Magnetic Permeability (20°C)<1.05
Young’s Modulus (kN/mm2)200
Specific Electrical Resistance, 20°C (µΩ-m)0.74
Mean coefficient of thermal expansion, 20-100°C (m/m/°C)16.5 x 10-6
Specific Heat, 20°C (J/kg.K)485
Thermal conductivity, 20°C (W/m.K)14

Product Features

Key Features:

  • Higher resistance to pitting corrosion and crevice corrosion in seawater than Alloy 304 stainless steel
  • Pitting Resistance Equivalent number (PREN) of 25 compared with 19 for Alloy 304
  • Excellent ductility and impact strength at both ambient and sub-zero temperatures
  • Low carbon version of Alloy 316 thereby immune from grain boundary sensitisation
  • Excellent forming and welding characteristics
  • Non-magnetic except after significant welding or cold working

Applications:

  • Process industry equipment in chemical containers, transport units, heat exchangers and organic & fatty acid production
  • Marine and shipbuilding piping, pumps, valves, fittings and marine architecture
  • Oil & Gas industry piping, valves, pumps, heat exchangers
  • Mining industry for woven screens
  • Machined parts for tube and pipe fittings
Datasheet S Sanmac 316L Hollow Bar (rev2) Langley Alloys Hollow Bar available sizes